Influence of filling materials on the fracture resistance of resin composite used for sealing screw access hole / Influência dos materiais de preenchimento na resistência a fratura das resinas compostas utilizadas para selamento do orifício de acesso ao parafuso

Introduction: Screw-retained restorations have a screw access hole (SAH) sealed with resin composite aiming at safe-guarding the aesthetic features of the ceramic veneer. The loss or wear of the resin composite applied in sealing the SAH is among the most common complications in implant prosthodontics, as the fracture of ceramic veneer. Objective: Evaluate the influence of sealant materials on the fracture resistance of resin composite applied in sealing screw access hole in screwed (SAH) implants. Material and method: The samples were produced from UCLA abutments in metallic NiCr alloy with subsequent application of ceramic. After asperisation and conditioning ceramic surface, was applied silane and dentin adhesive, before sealing the conduits with resin composites Z100 and P60. Nine groups (n=10) were evaluated: sealing with Z-100 (ZNC) and P-60 (PNC) without obturation of SAH; sealing with Z100 (ZCP) and P-60 (PCP) with absorbent cotton; Z100 (ZPT) and P60 (PPT) with polytetrafluoroethylene; Z100 (ZGP) and P60 (PGP) with gutta-percha and a cemented ceramic crown (ICS). After the fracture resistance test, the data were analyzed using two-way ANOVA and Tukey HSD tests (p<.05). Result: The fracture mode was evaluated by scanning electron microscope. Irrespective of the filling material, the highest mean values of fracture resistance were observed in the sealing with P60 (p=.002). When combined with resins composed of a sealing material, the results obtained were: ZGP: 805.5N/ PGP: 929.5N

Introdução: As próteses parafusadas possuem orifício de acesso ao parafuso (SAH), os quais são selados com resina composta. Sua perda ou desgaste está entre as complicações mais comuns em próteses sobre implantes, associadas a fratura da lâmina cerâmica. Objetivo: Assim, é importante avaliar a influência dos materiais de selamento na resistência à fratura de resina composta aplicada ao SAH no selamento de prótese sobre implantes parafusadas. Material e método: As amostras foram produzidas utilizando pilares UCLA em liga metálica de NiCr com posterior aplicação de cerâmica. Após asperização e condicionamento da superfície cerâmica, foram aplicados silano e adesivo dentinário, antes da selagem dos condutos com as resinas compostas Z100 e P60. Foram avaliados nove grupos (n = 10): selamento com Z-100 (ZNC) e P-60 (PNC) sem selamento do SAH; selamento com Z100 (ZCP) e P-60 (PCP) com algodão absorvente; Z100 (ZPT) e P60 (PPT) com politetrafluoroetileno; Z100 (ZGP) e P60 (PGP) com guta-percha e coroa de cerâmica cimentada (ICS). Após o teste de resistência à fratura, os dados foram analisados usando ANOVA de dois fatores e testes Tukey HSD (p<0,05). O tipo de fratura foi avaliado por microscópio eletrônico de varredura. Resultado Independentemente do material obturador, os maiores valores médios de resistência à fratura foram observados no selamento com P60 (p=0,002). Quando combinados com resinas compostas por um material de selamento, os resultados obtidos foram: ZGP: 805,5N/ PGP: 929,5N

Influence of Cusp Inclination and Type of Retention on Fracture Load of Implant-Supported Crowns

Abstract There are few informations about the influence of cusp inclination on the fracture strength of implant-supported crowns. The study aimed to evaluate the influence of cusp inclination and retention type on fracture load in implant-supported metal-ceramic single crowns. Sixty crowns were made, classified as cemented and screw-retained with screw access hole (SAH) sealed or not. Standard (33°) and reduced (20°) cusp inclinations were tested for each group (n=10). To support crowns of a mandibular second molar, analogs of external hexagon implants 5.0 were used. The fracture load was measured in a universal testing machine EMIC DL2000 (10 kN load cell; 0.5 mm/min). Two-way ANOVA (retention and cusp inclination) followed by post hoc Tukey’s honest significant difference test was used for the statistical analyses (a=0.05). Crowns with reduced cusp inclination exhibited significantly higher fracture load (p<0.01) than crowns with standard cusp inclination. Cemented crowns showed significantly higher fracture load (p<0.01) than screw-retained crowns. The interaction among these factors was not significant (p>0.05) for the fracture load. The sealing of SAH did not influence the fracture load of screw-retained crowns (p>0.05). In conclusion, fracture load of implant-supported metal-ceramic crowns was influenced by retention and cusp inclination, and there was no influence of the sealing of SAH.

Resumo Existem poucas informações sobre a influência da inclinação de cúspide na resistência à fratura de coroas implantossuportadas. O objetivo do estudo foi avaliar a influência da inclinação de cúspide e do tipo de retenção na carga de fratura de coroas unitárias metalocerâmicas implantossuportadas. Sessenta coroas foram confeccionadas, classificadas como cimentadas e parafusadas com orifício de acesso ao parafuso selado ou não. Cúspides com inclinação padrão (33°) e reduzida (20°) foram testadas para cada grupo (n=10). Para suportar as coroas de um segundo molar inferior, análogos de implante hexágono externo 5.0 foram utilizados. A carga de fratura foi mensurada em máquina de ensaios universais EMIC DL2000 (célula de carga de 10 kN; 0,5 mm/min). ANOVA dois fatores (retenção e inclinação da cúspide) seguido do pós-teste de Tukey da diferença honestamente significativa foi utilizada para análise estatística (a=0,05). Coroas com inclinação de cúspide reduzida exibiram carga de fratura significativamente maior (p>0,05) que coroas com cúspides de inclinação padrão. Coroas cimentadas apresentaram carga de fratura significativamente maior (p<0,01) que coroas parafusadas. A interação entre os dois fatores não foi significante (p>0,05) para a carga de fratura. O selamento do orifício de acesso ao parafuso não influenciou a carga de fratura das coroas parafusadas (p>0,05). Concluindo, a carga de fratura de coroas metalocerâmicas implantossuportadas foi influenciada pelo tipo de retenção e inclinação da cúspide, e não houve influência do selamento do orifício de acesso ao parafuso

Effect of Glaze Cooling Rate on Mechanical Properties of Conventional and Pressed Porcelain on Zirconia

Abstract The aim of this study was to characterize a conventional and a pressed porcelain for zirconia core as to biaxial flexural strength (BFS), apparent fracture toughness (FT) and microstructure composition, and to investigate the effect of glaze cooling rate on the BFS of the zirconia/porcelain bilayers. Monolayers of conventional porcelain Vita VM9 and pressed porcelain Vita PM9 (n=15) (12 mm diameter x 1.2 mm thick) were prepared for the BFS test (MPa). Apparent fracture toughness (MPa.m1/2) was measured by indentation technique (n=15). t-Student test was performed for statistical analysis. Scanning electron microscopy and x-ray diffraction were used to analyze the porcelain's microstructure. For the BFS of bilayers, zirconia discs (12 mm diameter x 1 mm thick) (Vita In-Ceram YZ) were veneered with the two porcelains (1 mm thick). After the glaze firing simulation, the specimens were submitted to fast or slow cooling (n=15). Apparent fracture toughness (MPa.m1/2) was measured on the porcelain surface of bilayers (n=15) and residual stress was calculated. Two-way ANOVA (porcelain and cooling method) was used for the bilayer analysis (a=0.05). Vita PM9 monolayer exhibited significantly higher BFS (p<0.01), but there was no significant difference (p=0.41) in the FT between the porcelains. For bilayer specimens, the two-way ANOVA for BFS was significant for the porcelain variable only (p<0.01) better for Vita PM9/zirconia. Two-way ANOVA for the FT for the bilayers was not significant for any variable. All groups showed compressive residual stresses. The pressed porcelain seems to be mechanically more effective for zirconia veneering.

Resumo Este estudo teve como objetivo caracterizar uma porcelana convencional e uma prensada indicadas para infraestrutura de zircônia em termos de resistência à flexão biaxial (RFB), tenacidade à fratura aparente (TF) e composição microestrutural, e investigar o efeito da taxa de resfriamento do ciclo de glaze na RFB de espécimes bicamada de zircônia/porcelana. Espécimes monocamada de porcelana convencional Vita VM9 e porcelana prensada Vita PM9 (n=15) (12 mm de diâmetro x 1,2 mm de espessura) foram preparados para o ensaio de RFB (MPa). Tenacidade à fratura aparente (MPa.m1/2) foi mensurada pela técnica da indentação (n=15). O teste de t-Student foi aplicado para as análises estatísticas. Microscopia eletrônica de varredura e difração de raios-X foram utilizadas para análise microestrutural da porcelana. Para o ensaio de RFB nos bicamadas, discos de zircônia (12 mm de diâmetro x 1 mm de espessura) (Vita In-Ceram YZ) foram recobertos com as duas porcelanas (1 mm de espessura). Após a simulação da queima de glaze, os espécimes foram submetidos ao método de resfriamento rápido ou lento (n=15). A tenacidade à fratura aparente (MPa.m1/2) foi mensurado na superfície da porcelana dos bicamadas (n=15) e o estresse residual foi calculado. Foi utilizado ANOVA a dois fatores (porcelana e método de resfriamento) para análise estatística dos espécimes bicamada (a=0,05). Monocamadas de Vita PM9 exibiram valores de resistência à flexão biaxial significativamente maiores (p<0,01), mas não houve diferença estatística (p=0,41) em relação à TF entre as porcelanas. Para os espécimes bicamada, ANOVA a dois fatores para RFB foi significante apenas para a variável porcelana (p<0,01), com superioridade para Vita PM9/zircônia. ANOVA a dois fatores para TF dos espécimes bicamadas não apresentou significância para nenhuma variável. Todos os grupos apresentaram estresse residual de compressão. Porcelanas prensadas parecem ser mecanicamente mais efetivas para recobrimento de zircônia.

Influence of Sealing of the Screw Access Hole on the Fracture Resistance of Implant-Supported Restorations

Abstract The purpose of this study was to assess the influence of sealing of the screw access hole (SAH) on the fracture resistance of metal-ceramic implant-supported restorations. UCLA abutments were used to make 30 implant-retained mandibular molar restorations and divide equally into three groups: Group SRS: screw-retained restorations with SAH sealed; Group SRNS: screw-retained restorations with SAH not sealed; Group CR: cement-retained restorations. The following protocol was adopted to restore the SAH: the ceramic surface of the SAH was air-abraded with aluminum oxide; etched with 10% hydrofluoric acid; a silane coupling agent and a bonding agent were applied; cotton pellets were used as filling material and P-60 resin composite as restoring material. The cement-retained restorations were cemented with Rely-X U100. A metal rod with a spherical tip of 6.0 mm diameter was used to apply a vertical static load, simultaneously on the buccal and lingual incline cusps, at a crosshead speed of 0.5 mm/min until the fracture of the specimens. Data were analyzed using one-way ANOVA and Dunnet test (p<0.05) for multiples comparisons. The mode of failure was evaluated by a scanning electron microscopy (SEM). No significant difference between screw-retained restorations was found. The highest mean fracture resistance values were observed with CR group. Therefore, it was shown that SAH sealing did not influence the fracture resistance of the screw-retained restorations.

Resumo O objetivo deste estudo foi avaliar a influência do selamento do orifício de acesso ao parafuso (OAP) na resistência à fratura de coroas metalocerâmicas implantossuportadas aparafusadas. Pilares UCLA foram utilizados para fazer 30 molares inferiores implantossuportados e divididos igualmente em três grupos: Grupo AS: coroas aparafusadas com o OAP selado; Grupo ANS: coroas aparafusadas com o OAP não selado; Grupo CC: coroas cimentadas. O seguinte protocolo foi utilizado para selar o OAP: a superfície de cerâmica do OAP foi jateada com óxido de alumínio; condicionada com ácido fluorídrico a 10%; um agente silano e um adesivo dentinário foram aplicados; bolinhas de algodão foram utilizadas como material de preenchimento e a resina composta P-60 como material de restauração. As coroas cimentadas foram cimentadas com Rely-X U100. Uma haste de metal com uma ponta esférica de 6.0 mm de diâmetro foi usada para aplicar uma carga estática vertical, simultaneamente nas vertentes triturantes das cúspides linguais e vestibulares, com 0,5 mm/min velocidade do atuador até a fratura das coroas. Os dados foram analisados através de ANOVA um fator e teste de Dunnett (p<0,05) para as comparações múltiplas. O modo de falha foi avaliado por um microscópio eletrônico de varredura (MEV). Não houve diferença significativa entre restaurações aparafusadas. Os maiores valores médios de resistência à fratura foram observados com o Grupo CC. Portanto, observou-se que o selamento do OAP não influenciou a resistência à fratura das coroas aparafusadas.